| TIDAK. | Sifat Resin | Nilai tipikal | Satuan | Metode Pengujian |
| 1 | Berat Jenis, 23℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Penyusutan Cetakan, 23℃, 3,2mm, 23℃ | 0,4-0,7 | % | ASTM D955 |
| 3 | Laju Aliran Lelehan, 220℃, 10kg | 22 | g/10 menit | ASTM D1238 |
| 4 | Kekuatan Tarik pada Titik Leleh, 23℃, 50mm/menit, 3,2mm | 49 | MPa | ASTM D638 |
| 5 | Perpanjangan Tarik pada Titik Leleh, 23℃, 50mm/menit, 3,2mm | 5 | %, (Min) | ASTM D638 |
| 6 | Perpanjangan Tarik Saat Putus, 23'℃, 50mm/menit, 3,2mm | 10 | %, (Min) | ASTM D638 |
| 7 | Modulus Tarik, 23℃, 50mm/menit, 3,2mm | 2350 | MPa | ASTM D638 |
| 8 | Kekuatan Lentur, 23℃, 15mm/menit, 3,2mm | 78 | MPa | ASTM D790 |
| 9 | Modulus Lentur, 23℃, 15mm/menit, 3,2mm | 2550 | MPa | ASTM D790 |
| 10 | Kekuatan Benturan Izod, Berlekuk, 3,2 mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Kekuatan Benturan Izod, Berlekuk, 3,2 mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Kekuatan Benturan Izod, Berlekuk, 6,4 mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Kekuatan Benturan Izod, Berlekuk, 6,4 mm, -30℃ | 90 | J/m | ASTM D256 |
| 14 | Kekerasan Rockwell, Skala R | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1,82MPa, 6,4mm, Tidak dianil | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/jam | 92 | °C | ASTM D1525 |
| 17 | RTI Listrik | 95 | °C | UL 746B |
| 18 | RTI Mekanik dengan Dampak | 95 | °C | UL 746B |
| 19 | RTI Mekanik tanpa Dampak | 95 | °C | UL 746B |
| 20 | Kemudahan terbakar, 1,5 mm | HB | / | UL 94 |
| 21 | Kemudahan terbakar, 3,0 mm | HB | / | UL 94 |